S275J0
Data under reviewS275J0 is the 0 °C impact-tested version of S275, specified where the structure sees sub-ambient service temperatures. Chemistry is held slightly tighter than S275JR to secure the low-temperature toughness.
Chemical composition
| Element | Content (%) |
|---|---|
| C | ≤0.18 |
| Mn | ≤1.50 |
| P | ≤0.030 |
| S | ≤0.030 |
Weight percent, per the governing standard ranges. Actual values per heat are on the mill certificate.
Properties
| Yield strength | ≥275 MPa (≤16 mm) |
| Tensile strength | 410–560 MPa |
| Impact | J0: 27 J at 0 °C |
| Density | 7.85 g/cm³ |
Heat treatment
Supplied hot rolled; no hardening treatment.
Equivalent grades
| Standard | Designation |
|---|---|
| din | 1.0143 (S275J0) |
Compare side by side: S275J0 vs S275JR
Equivalents overlap in chemistry and use but are not always identical — see our equivalents guide before substituting in certified designs.
Applications & Processing
Applications: Outdoor structures in cold climates, transport equipment, towers.
Processing: As S275JR; the J0 impact grade does not change welding practice.