8615
Data verified8615 is the low-carbon member of the 86xx triple-alloy carburizing family, sharing 8620 alloy content at slightly lower carbon. It is chosen for small gears and parts where a ductile core is paramount.
Chemical composition
| Element | Content (%) |
|---|---|
| C | 0.13–0.18 |
| Si | 0.15–0.35 |
| Mn | 0.70–0.90 |
| P | ≤0.035 |
| S | ≤0.040 |
| Cr | 0.40–0.60 |
| Ni | 0.40–0.70 |
| Mo | 0.15–0.25 |
Weight percent, per the governing standard ranges. Actual values per heat are on the mill certificate.
Properties
| Case hardness (carburized) | 58–62 HRC |
| Core tensile strength | 650–900 MPa (typ.) |
| Density | 7.85 g/cm³ |
Heat treatment
Carburize 900–930 °C; quench 820–850 °C oil; temper 150–200 °C.
Equivalent grades
| Standard | Designation |
|---|---|
| aisi | 8615 |
Compare side by side: 8615 vs 8620 · 8615 vs 8617 · 8615 vs 5120
Equivalents overlap in chemistry and use but are not always identical — see our equivalents guide before substituting in certified designs.
Applications & Processing
Applications: Small gears and pinions, bushings, transmission parts.
Processing: Excellent machinability and carburizing response.