316L vs 317L
These two grades are listed as equivalents of each other: their chemistry windows overlap and they serve the same applications. They are not always identical — check the differences below before substituting, especially in certified designs.
316L
Stainless Steel
316L is the low-carbon version of 316 and the most specified molybdenum-bearing stainless for welded equipment. It combines chloride pitting resistance with freedom from weld sensitisation.
Standards: DIN 1.4404 · AISI 316L · JIS SUS316L · GB 022Cr17Ni12Mo2
317L
Stainless Steel
317L is the low-carbon version of 317, with 3–4% molybdenum for welded equipment in hot chloride and acid service beyond the capability of 316L. Its PREN of about 30 bridges the gap to super-austenitic grades.
Standards: DIN 1.4438 · AISI 317L · JIS SUS317L · GB 022Cr19Ni13Mo3
Chemical composition compared (%)
| Element | 316L | 317L |
|---|---|---|
| C | ≤0.030 | ≤0.030 |
| Si | ≤0.75 | ≤0.75 |
| Mn | ≤2.00 | ≤2.00 |
| P | ≤0.045 | ≤0.045 |
| S | ≤0.030 | ≤0.030 |
| Cr | 16.00–18.00 | 18.00–20.00 |
| Ni | 10.00–14.00 | 11.00–15.00 |
| Mo | 2.00–3.00 | 3.00–4.00 |
| N | ≤0.10 | ≤0.10 |
Properties compared
| Property | 316L | 317L |
|---|---|---|
| Delivery condition | Annealed | Annealed |
| Hardness | ≤217 HB (annealed) | ≤217 HB (annealed) |
| Tensile strength | 485–690 MPa | 515–690 MPa |
| Yield strength | ≥170 MPa | — |
| Density | 7.90 g/cm³ | 7.90 g/cm³ |